The influence of Ru additions on the corrosion properties of WC-Co-Cr hard metals

Simple item page
dc.contributor.authorNelwalani, Ndivhuwo Brayner
dc.date.accessioned2019-11-12T08:43:15Z
dc.date.available2019-11-12T08:43:15Z
dc.date.issued2019
dc.descriptionA dissertation submitted to the faculty of Engineering and the Built Environment, University of the Witwatersrand, Johannesburg, in fulfillment of the requirements for the degree of Master of Science in Engineering. Johannesburg, May 2019en_ZA
dc.description.abstractThe aim of this research was to study the effect of adding Ru to WC-10Co-4Cr coating and determining the effect there of on corrosion properties, wear properties and tribo-corrosion properties of the coatings. The Ru powder was added to the 1350 VM/WC-731-1 powder in different concentrations ranging from 0.5wt% to 2wt%. The 1350 VM/WC-731-1 powder, which had a composition of WC-10wt%Co-4wt%Cr was mixed together with Ru powder for several hours before thermally coated on a steel substrate. The powders morphologies were characterized using Field Emission Scanning Electron Microscope (FESEM). The thermal coating method used was the High Velocity Oxygen Fuel (HVOF). After successful coating, the samples were sectioned to smaller pieces and different test were done on the smaller pieces to determine coating properties. FESEM characterization on coating morphologies were done before any test were performed and post-test FESEM characterization were also performed after each test. On the results obtained, it was evident that the Ru addition had an effect of decreasing the hardness by very low margin. The microstructural analysis showed no to very little effect caused by Ru addition on the powder. The distribution of Ru on the coatings were not constant and it was distributed in small pockets or islands throughout the coatings. Two very corrosive environments, which were composed of synthetic mine water, at pH levels of 3 and 1, were used as corrosion electrolyte and tribo-corrosion electrolyte. The corrosion open circuit potential showed a positive results as the increase in Ru content had an effect of decreasing the corrosion potential. The wear rate of the coating decreased with increasing Ru content and the coefficient of friction also increased with increasing Ru content. Tribo-corrosion rates decreased with increase in Ru content in the coatingen_ZA
dc.description.librarianMT 2019en_ZA
dc.identifier.urihttps://hdl.handle.net/10539/28415
dc.language.isoenen_ZA
dc.titleThe influence of Ru additions on the corrosion properties of WC-Co-Cr hard metalsen_ZA
dc.typeThesisen_ZA
Files
Original bundle
Now showing 1 - 2 of 2
No Thumbnail Available
Name:
MSc ABSTRACT NB Nelwalani.pdf
Size:
29.89 KB
Format:
Adobe Portable Document Format
Description:
Download
No Thumbnail Available
Name:
MSc Material science dissertation 2019 (NB Nelwalani).pdf
Size:
7.54 MB
Format:
Adobe Portable Document Format
Description:
Download
License bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
license.txt
Size:
1.71 KB
Format:
Item-specific license agreed upon to submission
Description:
Download
Collections
ETD Collection