School of Chemistry (ETDs)
Permanent URI for this communityhttps://hdl.handle.net/10539/38001
Browse
50 results
Search Results
Item A systematic study on the use of the sol-gel synthetic method for lithium manganese oxide-based cathode materials(University of the Witwatersrand, Johannesburg, 2024-09) Muntswu, Zwivhuya; Billing, Caren; Ferg, Ernst E.; Billing, David G.This dissertation investigated the synthesis of two lithium manganese oxide-based cathode materials (Li1.03Mn1.97O4 and LiAl0.4Mn1.6O4) using the sol-gel method and probing the phase transitions during the synthesis. The sol-gel synthetic method involved dissolving stoichiometric amounts of lithium nitrate, manganese nitrate hydrate, and citric acid in distilled water forming an aqueous solution. The starting precursor materials were dried at 140 °C which formed a crystalline phase of -Aqua-S-citrato (2-)-manganese(II) with an orthorhombic crystal system and P222 space group. The thermal behaviour of the precursor was explored to understand the effects of calcination/annealing temperatures. Thermal analysis of precursors prepared using nitrate salts with a 1:1 total metal ion to citric acid ratio displayed thermal stability to temperatures higher than 380 °C with the formation of a final metal oxide after 70% mass loss due to the decomposition of the organic and nitrate materials. However, when increasing the concentration of the complexing agent, an increase in material decomposition due to an increase in organic material is seen. The precursor materials prepared with a lower complexing agent concentration result in materials that have thermal instability when exposed to high temperatures. Thermal analysis of Li1.03Mn1.97O4 and LiAl0.4Mn1.6O4 prepared using acetate salts as starting materials shows material decomposition at high temperature of ~600 °C Calcining both undoped and Al-doped nitrate precursors at moderate temperatures (380 °C to 500 °C) resulted in the formation of Li1.03Mn1.97O4 and LiAl0.4Mn1.6O4 with a pure cubic spinel structure and an Fd-3m space group, however, increasing the calcining temperature to 800 °C for the undoped nitrate-based precursor revealed an impurity phase formation relating to dilithium manganese oxide with a monoclinic crystal system. On the other hand, calcining acetate-based precursors at moderate temperatures (380 °C to 500°C) results in metal oxides with low crystallinity compared to metal oxides prepared with nitrate-based precursors. Calcining acetate-based precursors at 800 °C was more favourable since they form the desired metal oxides without any impurities which might imply structural phase stability at high temperatures. The local and average crystallographic structures (via PDF and XRD respectively) of various nitrate-based metal oxides were investigated, where a good agreement between collected data and a calculated structural model revealed the formation of a cubic spinel structure of space group Fd-3m. Li1.03Mn1.97O4 and LiAl0.4Mn1.6O4 metal oxides were achieved from calcining precursors at moderate temperatures of 380 °C and 450 °C. The PDF high r-value signal displays a good fit which confirms to the average structure data information where the r-value signal which correspond to the local structure refinements have a minor discrepancy when fitted with a cubic spinel of space group Fd-3m.Item Synthesis and electrochemical properties of high-entropy spinel oxides, cobalt atomic clusters and zinc oxide as electrode materials for rechargeable zinc-air batteries(University of the Witwatersrand, Johannesburg, 2024-07) Gaolatlhe, Lesego; Ozoemena, Kenneth IkechukwuThis thesis investigated cathode and anode electrode materials for application in rechargeable zinc-air battery (RZAB). Two types of cathode materials were strategically studied in RZAB applications: (a) cobalt carbon composites of (i) cobalt atomic clusters (Co AC@CBPDC) and (ii) cobalt nanoparticles (Co NP@CBPDC), and (b) high-entropy spinel oxide (HESOx, containing five transition metals – Cu, Mn, Fe, Ni, and Co). The activities of these materials toward oxygen reduction reaction (ORR and oxygen evolution reaction (OER) were investigated in both half- and full-cell configurations as a proof-of-concept in RZAB cells in alkaline electrolyte. Considering that conventional zinc plate has several short-comings as an anode for RZAB, a new material, polydopamine-derived carbon-coated zinc oxide (ZnO@PDA-DC), was also synthesised and applied in RZAB as a possible alternative anode to the popular zinc plate. First, Co AC@CBPDC and Co NP@CBPDC were prepared using the metal-organic framework (MOF) route through the microwave-assisted solvothermal method and acid treatment. From the XRD results, the spectra showed dominant {111} and {200} phases, characteristic of metallic cobalt with a face-centred cubic (fcc). There were trace amounts of CoO observed indicating the coexistence of Co/CoO. From TEM imaging, Co AC@CBPDC was highly defective with a visible porous carbon structure than its counterpart (Co NP@CBPDC) and showed dispersed atomic clusters. BET data showed that Co AC@CBPDC had a higher surface area (144.8 m2/g) than the Co NP@CBPDC (33.25 m2/g). The improved physicochemical merits of the Co AC@CBPDC allowed for better ORR and OER activities than the Co NP@CBPDC in terms of low halfway potential (E1/2), onset potential (Eonset), overpotential at 10 mA/cm2 (ƞ10), potential gap (∆E) between the overpotential of OER and the halfway potential, and a higher kinetic current density (jk). The enhanced electrochemistry of the Co AC@CBPDC was attributed to the defects created by the acid treatment. As proof of real-life applicability, the Co AC@CBPDC electrocatalyst delivered an excellent air cathode in a parallel plate RZAB cell with notable OCV (1.23 V), peak power density (49.9 mW/cm2), a real energy density (477 mAh/cm2), long-term stability for 210 h, enhanced voltage retention, Coulombic efficiency (ca. 100 %) and DOD (51.3%), comparable to literature. In addition, an all-solid-state RZAB based on the Co AC@CBPDC catalyst gave a higher and constant OCV (1.73 V) at varied bending angles (0 – 180 degrees) and excellent stability. Second, new HESOx materials were prepared via the Pechini method at two different annealing temperatures of 500 and 750 oC (abbreviated herein as HESOx-500 and HESOx-750). P-XRD results showed that these are inverse spinel oxides, with {311} as the dominant phase. HR-TEM images proved that they are single nanocrystalline materials. XRD and BET data showed that the HESOx-500 is smaller in size, more porous, and has a higher surface area than its counterpart (HESOx-750). HESOx-500 showed superior ORR performance with an onset potential of 0.93 V and a E1/2 of 0.88 mV. The OER performance also showed improved ƞ10 compared to IrO2 with an overpotential of 340 mV at a current density of 10 mA/cm2, and a 45 ± 5.0 mV/dec Tafel slope, above the performance of IrO2 (66 ± 6.1 V/dec). The ∆E of HESOx-500 was 0.69 V. The material was further tested as a cathode material in a RZAB cell. The optimised RZAB cell showed remarkable performance with a theoretical potential of 1.67 V and long-term stability of 375 h at 10 mA/cm2. The performance was attributed to the high-entropy compositional design with a high number of surface oxygen vacancies and different metal oxidation states. Finally, having dealt with the issue of bifunctionality in RZAB, a new ZnO@C anode material was also considered. The ZnO@PDA-DC (where PDA-DC means polydopamine-derived carbon) was used due to its ability to form Zn2+ pathways. Electrochemical potentiodynamic polarisation tests were performed to understand and compare the corrosion inhibition effects in an alkaline medium (6 M KOH). The ZnO@PDA-DC showed better corrosion inhibition properties than the zinc plate and other samples: low corrosion current (icorr = 0.107 uA/cm2) and corrosion potential (Ecorr = 1.077 V), and a mixed inhibition effect, indicating reduced hydrogen evolution reaction and zinc dissolution. Due to the excellent corrosion inhibition properties of the ZnO@PDA-DC, it was then evaluated in the RZAB cell. The shallow galvanostatic charge-discharge cycle stability at 2 mA/cm2 was able to maintain 150 h in a RZAB at a voltage gap of 0.76 V to 0.80 V. The results demonstrated that enhanced rechargeability is possible with ZnO@PDA-DC for RZAB.Item Synthesis of platinum-based electrocatalysts using nitrogen doped onion-like carbon and WS2 composites as the support for electrooxidation of ethanol in direct alcohol fuel cells(University of the Witwatersrand, Johannesburg, 2024-10) Bila, Laercia Rose; Gqoba, Siziwe; Maubane-Nkadimeng, Manoko S.The study reports on the synthesis of onion-like carbons (OLCs)/tungsten disulfide (WS2) composites as catalyst support for direct alcohol fuel cells (DAFC). OLCs were synthesized using waste engine oil over a flame pyrolysis (FP) method. The pristine OLCs (p-OLCs) were functionalized and purified using nitric acid (HNO3). The functionalized OLCs (F-OLCs) were further doped with nitrogen using melamine to increase the electronic properties of the OLCs. WS2 was synthesized using the colloidal method and oleylamine was used as the capping agent. Pt/p-OLCs, Pt/F-OLCs, and Pt/N-OLCs were synthesized using a reflux method where ethylene glycol was the reducing agent. Finally, WS2/N-OLCs were synthesized using the colloidal method and then Pt was dispersed on WS2/N-OLCs to form Pt/WS2/N-OLCs. High-resolution transmission electron microscopy showed the presence of onion-like rings in the OLCs and the quasi-spherical morphology, while a flower-like morphology was observed for WS2. Powder X-ray diffraction revealed that the synthesized WS2 had traces of WO3 due to the oxidation of WS2 which introduces WO3 impurities. Energy Dispersive X-ray Spectroscopy revealed that the OLCs derived from waste engine oil present some impurities that were attributed to the motor wear as well as the fuel. When Pt was loaded onto the WS2/N OLCs composite, the WS2 lost its original nanoflower morphology, which was attributed to the presence ethylene glycol used as a reducing agent. X-ray photon spectroscopy confirmed the successful synthesis of the Pt electrocatalysts. Cyclic voltammetry was used to determine the oxidation of ethanol and the current density of the synthesized electrocatalysts. Interestingly, the Pt/p-OLCs electrocatalyst had a higher current density compared to Pt/F-OLCs and Pt/N-OLCs. This was attributed to metal impurities found in p-OLCs, which were reduced during the purification process. The Pt/WS2/N-OLCs electrocatalyst showed higher current density compared to Pt/WS2 but this was low compared to Pt/N-OLCs. The data reveals that the addition WS2 shows a co-catalyst behaviour, rather than a support.Item Biocatalytic oxidative conversion of valencene to nootkatone mediated by lipoxygenase and cytochrome P450(University of the Witwatersrand, Johannesburg, 2024-03) Raboya, Christopher; Ngwira, Kennedy; Brady, DeanNootkatone (NK) is an oxygen-containing sesquiterpene with a significant grapefruit aroma and plays an important role in the flavour and fragrance industry. The natural production of NK through extraction produces trace amounts and is therefore not a viable option to meet industrial needs. The chemical synthesis often utilises reagents harmful to the environment. The purpose of this research was to explore the use of crude lipoxygenase (LOX) enzyme extracted from soya beans, commercial mutants of CYP450 as well as laccase enzymes for the conversion of valencene (VL), the aroma components of citrus fruits to NK. For the LOX reactions, a conversion of 28.79% (mol/mol) was obtained when the reactions were performed with LOX only. The best conversion of 74.46 % was realised when FeSO4.7H2O and MnSO4 were added to the reaction. In the temperature studies, 70 ˚C was shown to be the optimal temperature for the conversion. In addition, we observed that vegetable oils provided sufficient unsaturated fatty acids to facilitate the conversion of VL to NK with sunflower oil being the best. In exploring the potential of LOX to oxidise other organic molecules, caryophyllene was oxidised to novel caryophyllene oxide, and styrene was oxidised to benzoic acid, 1-phenylethane-1,2-diol, and 2-hydroxyl-2-phenylethyl benzoate. This is the first time that such oxidations are reported, and this underlines the potential of LOX in biotransformation and organic synthesis. For CYP450 reactions, the best conversion of 16.70 % was obtained using a variant sourced from Prozomix. Evaluation of parameters such as temperature, pH (7.0 to 7.5), using buffer solutions should be explored to optimise the activity of the enzyme. Laccase from Novoprime Base 268 showed no activity for the conversion of VL to NK despite making use of mediators. Therefore, we should explore changing the reaction conditions, varying the pH of the reaction, buffer strength or mediator and laccases from other sources such as Cerrena unicolor and Trametes versicolor, as well as a fresh batch of laccase from Trichoderma (Merck) should be assessed in the conversion of VL to NK.Item Preparation of nitrogen-doped multiwalled carbon nanotubes anchored 2D platinum dichalcogenides for application as hydrogen evolution reaction catalysts(University of the Witwatersrand, Johannesburg, 2024-09) Mxakaza, Lineo Florence; Moloto, Nosipho; Tetana, ZikhonaThe alkaline hydrogen evolution reaction (HER) (H2O + 2e − → H2 + 2OH−) is fast gaining traction as a sustainable hydrogen gas generation route but suffers from slow reaction kinetics because of the additional water dissociation step and large reaction overpotential. As such, the current state-of-the-art acidic medium Pt and Ru catalysts suffer from considerable loss of catalytic activity in an alkaline medium. We propose the development and use of platinum metal dichalcogenides for alkaline HER. Platinum dichalcogenides are 2D materials that offer the advantage of more exposed catalytic sites, show dramatic chalcogen-dependent electronic properties, and have a band gap (0.24 eV - 1.8 eV for PtS2 and PtSe2) thus extending the use of these materials to light-stimulated photo-electrochemical (PEC) HER. As such, PtS2 is reported to be a semiconductor, PtSe2 is semi-conductive/semi-metallic depending on the number of layers, and PtTe2 is metallic. The Pt-chalcogen covalent bond intensifies down the chalcogen group. Additionally, the interlayer interactions in Pt dichalcogenides are covalent, and just like the Pt-chalcogen bond, intensify as the chalcogen atom changes from sulphur to selenium to tellurium. This behaviour of Pt dichalcogenides results from the Pt bonding d orbitals and the chalcogen bonding p orbitals that are relatively close in energy than in other TMDs, and the difference in the energy becomes smaller and smaller down the chalcogen group. Herein, we report on the synthesis of PtSe2 and PtTe2 using the colloidal synthesis method for the first time and then applying them as electrocatalysts in alkaline HER. As mentioned, developing 2D materials results in band gap development, particularly in PtS2 and PtSe2. Following this, PtSe2 was explored as a photocathode in light-induced photo-electrochemical HER. Generally, semiconductors are poor electron transporters and one of the major requirements for an efficient PEC cathode is solar absorption, charge generation, and efficient charge separation. The charge separation properties of PtSe2 were improved by supporting this material on highly conductive, mechanically, and thermally stable nitrogen-doped multi-walled carbon nanotubes (N-MWCNTs). In Chapter 3, we report on the effect of varying selenium precursors from elemental selenium, sodium selenite to selenourea on the colloidal synthesis of PtSe2 in a mixture of oleylamine and oleic acid at 320 ℃. All the reactions resulted in the formation of PtSe2 although PtSe2 prepared from selenourea is amorphous, evidenced by relatively broader XRD peaks and a smaller crystallite size. HER activity of the three PtSe2 catalysts was evaluated in 1 M KOH at a scan rate of 5 mV/s and PtSe2 prepared from selenium exhibited the earliest onset potential of 46 mV, overpotential of 162 mV, and a smaller Tafel slope of 112 mVdec-1. This material exhibits the smallest resistance to electron transport and a high electrochemical surface area. We then explored the effect of altering tellurium precursor from elemental tellurium to tellurium tetrachloride, and sodium tellurite. Unlike the PtSe2 synthesis, different platinum tellurite phases, PtTe2, PtTe, and the mixed phase PtTe: PtTe2 were produced from Te, PtCl4, and sodium tellurite, respectively. Of the three, PtTe2 exhibited the highest alkaline HER activity with an onset potential of 29 mV, an overpotential of 107 mV, and a Tafel slope of 79 mVdec-1. In the same chapter, we compared the catalytic activity of PtSe2 (prepared from Se) and PtTe2 (prepared from Te) catalysts. We determined that PtTe2 has a high surface roughness and electrochemical surface, leading to relatively higher activity than PtSe2. However, PtTe2 is metallic and therefore does not have a band gap, which implies that it cannot be employed in light-stimulated catalysis reactions. In Chapter 4, we explored the use of PtSe2 as a light-stimulated PEC alkaline HER catalyst. We used in situ colloidal synthesis to grow PtSe2 on the walls of N-MWCNTs to improve the overall electron transport properties of PtSe2. PtSe2 anchored on N-MWCNTs was also studied in the dark and under illumination using 1 sun (100 mW/cm2) to determine the influence of light on the HER catalytic activity of the hybrid materials. This study demonstrates that the light-stimulated HER activity of PtSe2 improves when minimal amounts of N-MWCNTs are incorporated in the PtSe2 sample matrix. This then leads to employing these materials as photocathodes in PEC HER.Item Synthesis and characterization of onion-like carbons for adsorption of tartrazine dye in water(University of the Witwatersrand, Johannesburg, 2024-08) Cwayi, Herbert Qaqambile; Maubane-Nkadimeng, Manoko S.; Coville, Neil J.; Maboya, Winny K.Industrial effluent often can contain a significant amount of synthetic dyes. The discharge of wastewater containing dyes into water streams without proper treatment consequently enters the soil and disturbs the aquatic and terrestrial life. Several wastewater treatment technologies have been proposed that can efficiently reduce the amount of synthetic dyes from the environment, in particular azo dyes. Among all the existing technologies for wastewater treatment, physical adsorption is a popular technology because it is inexpensive, simple, and efficient. The aim of this study is to synthesize, modify, and characterize onion-like carbons (OLCs) derived from four different waste oils for the adsorption of tartrazine dye in water. The OLCs derived from different carbon precursors (waste household oil, restaurant waste oil, engine waste oil, and paraffin oil bath waste) were synthesized using a flame pyrolysis method. The synthesized materials were doped with nitrogen using a chemical vapor deposition technique using 10% ammonia gas as a source of nitrogen. The N-doped OLCs were attached with hydroxyl groups through oxidation reactions to improve their solubility and adsorption efficacy. According to the high-resolution transmission electron microscopy and scanning electron microscopy images, the OLCs from all four-carbon precursor were quasi-spherical, agglomerated, and presented a chain-like structures of multi-layers. The distance between the graphitic layers was found to be 0.32 nm. The average particle size of OLCs was calculated to be 40.2 ± 2.5 nm. Adsorption studies revealed that the initial dye concentration, contact time, and pH of the dye solutions influenced the adsorption capacity of the tetrazine. Nitrogen doping of OLCs increased its capacity to adsorb the tartrazine dye. The nitrogen doped OLCs from household waste oil (H-N-OLCs) and engine waste oil (E-N- OLCs) were used in equilibrium adsorption studies in this work. For a concentration of 20 mg/L of tartrazine dye, an adsorption capacity of 28.9 mg/g was achieved using the N- doped OLCs from household waste oil. The adsorption process follows the pseudo second- order kinetic model. The adsorption isotherm is best fitted to the Freundlich mathematical model. The results obtained show that, the source of oil did not have major effect on the physicochemical properties of OLCs and that incorporation of nitrogen onto carbon matrix enhanced the adsorption of the anionic tartrazine dye in aqueous solution.Item Microwave-assisted synthesis of palladium-based ferroalloy electrocatalysts for application in alkaline direct alcohol fuel cells(University of the Witwatersrand, Johannesburg, 2024-11) Ramashala, Kanyane Nonhlanhla Eugenia; Billing, Caren; Modibedi, R. Mmalewane; Ozoemena, Kenneth IkechukwuThis research work describes the study of Pd-based ferro-electrocatalysts for application towards direct ethanol fuel cells (DEFCs), direct ethylene glycol fuel cells (DEGFCs), direct glycerol fuel cells (DGFCs) and oxygen reduction reaction (ORR) operated in a basic environment. The initial part of the research was to explore the Pd-based monometallic and bimetallic (Pd/C and PdFe/C) by utilising varied methods such as the conventional sodium borohydride (NaBH4) and microwave-assisted technique (MW) towards the oxidation of glycerol (gly), intending to choose the best method viable for these catalysts. This study revealed that MW techniques tuned the physicochemical properties of Pd/C and PdFe/C by augmenting their crystallinity and defect. These led to improved electrocatalytic activities towards glycerol oxidation reaction (GOR) over NaBH4 technique. MW process as a powerful tool was further used in the entire study to synthesise bimetallic and trimetallic electrocatalysts in ethanol (EtOH), ethylene glycol (EG) and glycerol (Gly) oxidation reaction in an alkaline environment. The synthesised bimetallic catalysts studied in this research work were (PdFe/C, PdCo/C, and PdMn/C) at varied ratios of Pd: M (Pd2M/C (2:1) and PdM/C (1:1)). Amongst them all, Pd2Fe/C and PdFe/C were observed to be the most favourable catalysts towards all the alcohols, with the excellent specific activity of about, for EtOH (11.59 and 4.15 mA cm-2), EG (9.82 and 5.51 mA cm-2) and Gly (8.94 and 4.73 mA cm-2), respectively. The satisfactory performance exhibited by the PdFe/C electrocatalyst prompted the exploration of the second 3d transition metal (PdFeMn/C and PdFeCo/C), intending to investigate the synergistic behaviour between the non-noble metals and Pd. The XRD confirmed that these electrocatalysts are in a crystalline nature with a decrease in d spacing (from 0.2247 nm, PdFe/C to 0.2236 nm (PdFeMn/C)) after the insertion of Mn into PdFe/C. This was supported by the TEM images obtained for the PdFeMn/C catalyst with a particle size of sub 10 nm. The comparison studies towards EtOH, EG and Gly were investigated for all the electrocatalysts and there was a remarkable observation, which is dissimilar from the theoretical studies (DFT). Density Functional Theory (DFT) revealed that PdFeCo performed better in terms of Gibbs free energy, binding energy, and energy band gap than PdFeMn; however, the experimental studies favoring the performance of PdFeMn. The PdFeMn/C delivered the best electrochemical activities, including a superior electrochemical active surface area (ECSA), larger current densities and mass activity response, and less susceptibility to poisoning and high conductivity as compared to PdFe/C and PdFeCo/C electrocatalysts. Furthermore, the PdFeMn/C electrocatalyst exhibited remarkable electrochemical properties during the ORR (basic medium). Ultimately, the best two anode electrocatalysts (PdFe/C & PdFeMn/C) were explored and tested for the proof-of-concept in the two-electrode configuration with the micro-3D printed cell. The PdFeMn/C delivered improved µ-ethylene glycol fuel cell, µ-glycerol fuel cell, and µ-ethanol fuel cell activities with respective to high voltage and power density of 33.27 mW cm-2, 11.00 mW cm-2 and 45,80 mW cm-2 respectively, operated at 100 mV / s. These electrocatalysts have demonstrated promising results in advancing ADAFCs.Item Towards the development and determination of trace impurities in battery grade nickel sulphate(University of the Witwatersrand, Johannesburg, 2024-10) Mabowa, Mothepane Happy; Tshilongo, James; Chimuka, LukeThis study introduces innovative research focused on developing and optimizing advanced extraction techniques for refining nickel hydroxide from secondary material solutions. This precursor to nickel sulfate is effectively purified through impurity removal and precise determination, enhancing the final product to battery grade standards. The research addresses the extraction of metal hydroxide from secondary sources such as spent batteries and industrial waste, promoting recycling and reducing environmental impact. By refining analytical methodologies and improving impurity control, this study advances the sustainable production of high quality nickel sulfate essential for advanced rechargeable batteries. The key challenge addressed in this study is the presence of impurities in secondary material solutions, which complicates the process of refining nickel hydroxide and hinders the production of high-purity nickel sulfate suitable for battery applications. Existing methods for recovering nickel from secondary materials are often inefficient, leading to high impurity levels, low recovery rates, and significant environmental impacts. Current methods such as solvent extraction and precipitation often fail to achieve the desired purity levels for nickel sulfate, necessary for use in high-performance battery manufacturing. Furthermore, these methods can be costly, resource-intensive, and environmentally damaging. Analytical methods used to measure impurities also have limitations. The complex and saturated matrix of battery-grade solutions challenges accurate impurity determination, often necessitating indirect methods such as difference analysis from nickel sulfate, which may not fully capture all impurity types or their concentrations. To resolve these issues the study focuses on optimizing advanced extraction techniques from these secondary sources. The research includes: (1) investigating the effectiveness of S-Curve precipitation by varying parameters such as pH levels, nickel concentration, precipitate dosage, temperature, impurity concentration, and solubility products; (2) evaluating solvent extraction for copper removal prior to nickel precipitation; (3) validating various analytical techniques (FAAS, EDXRF, ICP-OES) for trace element analysis; (4) examining lime precipitation for the removal of iron, manganese, and copper; and (5) characterizing β-nickel hydroxide (Ni(OH)₂) using scanning electron microscopy (SEM), X-ray diffraction (XRD) patterns, Fourier-transform infrared spectroscopy (FTIR), and X-ray photoelectron spectroscopy (XPS). The research employed a combination of precipitation methods, solvent extraction, and advanced analytical techniques. The S-curve precipitation of nickel hydroxide was optimised by varying pH levels, nickel concentration, and temperature. The study also examined lime precipitation as a method for impurity removal and used solvent extraction for copper removal before nickel recovery. Various solvents with different ratios were utilized at room temperature for copper extraction, and the 1:5 ratio of 5,8-diethyl-7-hydroxydodecan-6-oxime (LIX 63-70) proved to be effective. Analytical tools like FAAS, EDXRF, and ICP-OES were employed to validate the concentration of trace impurities, and techniques such as SEM, FTIR, XRD, and XPS were used to characterize the crystalline structure and purity of β-Ni(OH)₂. The first part of the work entailed devising a technique to extract base metals, specifically nickel, from the waste stream resulting from the nickel sulphide-fire assay waste. This study explores the recovery of nickel (Ni) through a combination of solvent extraction and precipitation techniques. The main objective is to develop an efficient process for separating Ni from copper (Cu) and iron (Fe) impurities, thereby optimising metal recovery at varying pH, concentration with addition of calcium hydroxide at 60˚C and contributing to the circular economy. The approach involves using LIX 63-70 for solvent extraction, which effectively loads Cu into the organic phase and allows for Ni liberation into the aqueous phase. Characterization of the S-curve precipitation process was carried out using various analytical techniques. The precipitation of Ni(OH)₂ was optimised at pH 6.5, as evidenced by X-ray diffraction (XRD) patterns, Fourier-transform infrared spectroscopy (FTIR), and X-ray photoelectron spectroscopy (XPS). The results show that Ni(OH)₂ precipitates in a crystalline β-phase, with XPS confirming the successful precipitation and minimal presence of Cu and Fe impurities at pH of 6.5 at 60˚C. Notably, the study also identifies the presence of Fe and Ca impurities at pH 2.5, as indicated by scanning electron microscopy (SEM), energy-dispersive X ray spectroscopy (EDX), and XRD analyses. The study addresses a critical research gap by providing a detailed assessment of the separation process for Ni from complex waste streams. It demonstrates the efficacy of 5,8-diethyl-7-hydroxydodecan-6-oxime (LIX 63-70) in selectively extracting Cu and reveals the influence of pH on the purity of Ni(OH)₂ precipitates. The process also involves significant lime consumption for neutralising the feed solution, with about 71% used to adjust the solution to pH 2.0, highlighting the importance of optimising reagent usage. The research presents a successful method for recovering Ni from fire assay waste in separating value-added metals from impurities. The findings contribute to advancements in metal recycling and repurposing, supporting the development of sustainable waste management practices and the promotion of a circular economy. Paper II evaluates the accuracy and reliability of elemental analysis in synthetic cathode liquor using Energy Dispersive X-ray Fluorescence (EDXRF) and Flame Atomic Absorption Spectroscopy (FAAS) with both factory default settings and after internal calibration and compares these results with those obtained from Inductively Coupled Plasma Optical Emission Spectroscopy (ICP-OES). The research aims to test the performance of EDXRF and FAAS for identifying and quantifying elements such as calcium (Ca), sodium (Na), cobalt (Co), iron (Fe), nickel (Ni), copper (Cu), arsenic (As), selenium (Se), antimony (Sb), and bismuth (Bi). The investigations into the impact of these parameters on the variations in absorbance for the targeted impurities guarantee satisfactory linearity and recovery. The recovery was quantified by comparing the concentration of elements in spiking samples and certified reference materials (CRMs) to known quantities, while the sensitivity of each method was assessed by the limits of detection (LOD). Linearity was assessed by constructing calibration curves at a variety of concentrations and calculating the coefficient of determination (R²) to guarantee precise results at varying concentration levels. Initial EDXRF results using default settings showed substantial inconsistencies, particularly with Ca, where measured values invariably showed 0 mg/L despite actual concentrations ranging from 0 to 0.15 mg/L, and Ni, where measured concentrations varied between 493,327 and 529,280 mg/L compared to the true value of 120,000 mg/L. After calibration, EDXRF displayed better accuracy for Co, Fe, and Cu but experienced limits with light elements like Se and Sb due to high LOD. FAAS demonstrated effective results for Co, Cu, Fe, and Mg but encountered limits, particularly in detecting low amounts of metals like Na. FAAS readings for Na demonstrated high variability with a standard deviation (SD) of 505.24 mg/L and a relative standard deviation (RSD) of 23.39%. Furthermore, differences in FAAS measurements for Ca, Fe, and Ni were seen, with fluctuations in standard deviation (SD) and relative standard deviation (RSD) suggesting a certain level of inconsistency. The ICP-OES results confirms the accuracy of FAAS by closely aligning with its measurements for elements such as Co and Ni. The precision of FAAS is further demonstrated by the low standard deviations (8.08 mg/L for Co and 4 mg/L for Ni) of ICP-OES results (e.g., Co: 990 mg/L, Ni: 126 mg/L). This validation underscores the dependability of FAAS to these components due to selection of FAAS for its cost-effectiveness and broad applicability in industrial analysis. Evaluation of numerous methods is crucial for a thorough evaluation of elemental analysis accuracy, as evidenced by the comparison with ICP-OES. In addition, it is crucial to distinguish between the discourse on analytical methods and recovery metrics, as recovery rates are more closely associated with preconcentration techniques than with the analytical methods themselves. This work aims to fill a significant research need by emphasising the need for internal calibration for EDXRF and the necessity of using several analytical methods in conjunction to obtain dependable results. It stresses the strengths and limits of each method, providing a complete approach to enhancing analytical accuracy in industrial applications. The study in Paper III investigates the characterisation and retrieval of β-Ni(OH)₂ from fire assay waste using chemical precipitation. Various analytical methods are used to confirm the successful synthesis and purity of the molecule. Nickel hydroxide (Ni(OH)₂) is a functionally diverse chemical with a broad spectrum of uses. A hexagonal crystalline structure of β-Ni(OH)₂ is confirmed by X-ray diffraction (XRD) analysis, therefore validating the successful precipitation procedure. Fourier-transform infrared spectroscopy (FTIR) spectra provide additional evidence for the presence of nickel hydroxide by displaying distinct peaks associated with υ(OH) and υ(NiO) bonds. The X-ray photoelectron spectroscopy (XPS) analysis reveals the significant Ni²⁺ oxidation peak, which confirms the successful precipitation at a pH of 6.5. Additionally, XPS analysis detects the presence of contaminants such as chlorine and calcium in the waste matrix. Scanning electron microscopy (SEM) shows layered granules with a predominantly transparent brucite analogue crystalline phase, typical of β-Ni(OH)₂. It also exposes rough textures and uneven aggregation, indicating increased oxide concentrations on the Ni surface. The presence of nickel (Ni) and oxygen (O), as well as calcium (Ca) impurities arising from the chemical precipitation process, is confirmed by energy-dispersive X-ray spectroscopy (EDX). An investigation of particle size distribution indicates an average particle size of 2.0 µm. The results of Inductively Coupled Plasma Optical Emission Spectroscopy (ICP-OES) indicate a reduction in Ni concentrations, with recorded values of 62.7 g/L in the pregnant leach solution, 0.8 g/L in the precursor solution, and 0.501 g/L in the solid precipitate (cake). The copper loading efficiency is measured to be 79%, accompanied by a nickel loss of 9.73% and a nickel recovery rate of around 90.27%. This effective separation process demonstrates a cost-efficient and environmentally responsible method for recycling nickel from acidic chloride media, underlining the broader potential for nickel reuse in industrial processes. This study conducts a comparative analysis of nickel oxide (NiO) that is derived from fire assay nickel sulphide (FA-NiS) and produced through chemical precipitation and sol-gel methods. The focus is on the structural, morphological, and sensing properties of the NiO. This research is significant in that it is the first to report on the application of NiO synthesised from waste materials for volatile organic compound (VOC) sensing. The primary goal is to clarify the distinctions in properties between NiO obtained through these methods and evaluate their suitability for environmental sensing applications. Nickel was initially extracted from the raffinate using 5,8-diethyl-7-hydroxydodecan-6-oxime. Subsequently, nickel hydroxide (Ni(OH)₂) was precipitated with lime (Ca(OH)₂) at pH levels of 2.5 and 6.5. The hydroxide was subsequently transformed into NiO through a thermal treatment process. The presence of nickel and oxygen at pH 6.5, as well as iron, nickel, and oxygen at pH 2.5, was verified through the use of scanning electron microscopy (SEM)-energy dispersive spectroscopy (EDS) and X-ray photoelectron spectroscopy (XPS). In both the sol-gel and chemical precipitation procedures, the X-ray diffraction (XRD) analysis demonstrated a cubic crystal structure with high average crystal sizes of 39-41 nm. The sol-gel process resulted in homogenous spherical particles, as evidenced by SEM imaging, whereas chemical precipitation resulted in aggregated layered grains. It is important to note that NiO precipitated at pH 2.5 exhibited coalesced hexagonal particles with a substantial amount of nickel and iron. The transition from nickel hydroxide to nickel oxide is essential because NiO is highly effective for VOC sensing due to its semiconductor properties. The study highlights the importance of utilising NiO in the detection of volatile organic compounds (VOCs) and the impact of each synthesis method on the material's sensory capabilities. Using certified reference materials, analytical methodologies, such as inductively coupled plasma optical emission spectrometry (ICP-OES) and X-ray fluorescence (XRF), demonstrated high-purity NiO (approximately 75%) with a low relative standard deviation (RSD <0.05%) and 90% recovery. The CRM AMIS 56 and SARM 33 were analysed alongside the samples to ensure reliable results were reproducible. Even at the lowest concentration of 1.5 ppm, NiO derived from fire assay waste demonstrated unambiguous sensing responses at 25˚C and 150˚C, with recovery times of 80 and 120 seconds, respectively. The potential of NiO from fire assay waste as an intriguing candidate for VOC sensing applications under ambient conditions was indicated by the highest response (Rg/Ra = 1.198 for 45 ppm ethanol) observed at 150˚C. The findings in paper IV highlight the suitability of nickel oxide synthesized from different methods for environmental sensing applications, particularly in volatile organic compounds detection. In Paper V, the focus is on the removal and characterization of impurities from pregnant nickel solutions at various pH levels, with an emphasis on enhancing nickel recovery and sustainable resource management. Lime is used as a precipitation agent to target impurities such as iron, lead, tin, manganese, and copper. The study employs inductively coupled plasma optical emission spectrometry (ICP-OES) to quantify and characterize these impurities. The objectives include improving analytical approaches for detecting trace contaminants, evaluating ICP-OES reliability for quality control, and assessing precipitation efficiency across different pH levels. Results reveal successful Fe3+ precipitation within the pH range of 2.0-3, alongside efficient manganese and copper precipitation at pH 5.5-6 and 4-6, respectively, aligning with established behaviours. The findings emphasise the significance of pH control for optimizing impurity removal from pregnant nickel solution, offering insights for enhancing nickel recovery processes in industrial settings. ICP-OES, supported by standard solutions and certified reference materials (CRMs), demonstrated exceptional linearity with correlation coefficients above 0.9995. The method showed high sensitivity, with detection limits and recoveries of CRM samples consistently within 10%. The study found that precipitation efficiency varies significantly with pH. Nickel (Ni) exhibited reduced precipitation at pH 2.02, with substantial precipitation occurring only at pH 6.5. Manganese (Mn) began precipitating at pH 2, achieving a peak removal efficiency of 98% at pH 6. Copper (Cu) precipitation started at pH 4, with a maximum efficiency of 99.3% between pH 4 and 6. Iron (Fe³⁺) was efficiently removed at pH 2.0-3.0. Significant variations in contaminant concentrations were observed, influenced by pH and precipitation agents. Fe³⁺ was removed with 100% efficiency at pH 2.5, while Cu precipitation was highly effective (99.3%) between pH 4 and 6. The decrease in Ni concentration at pH 2.02 was attributed to interactions with other metals rather than direct Ni precipitation. SEM revealed the morphology of the precipitates, showing a cauliflower-like structure for Ni(OH)₂ at pH 6.5 and the EDX confirmed the elemental composition of the precipitates, including Fe, Cu, Ni, Sn, Si, Al, Cl, Ca, and hydroxyl groups (OH), highlighting the presence of impurities precipitated at pH 2.5. This research highlights the effectiveness of ICP OES and EDX in trace impurity analysis and provides insights into optimizing precipitation processes, contributing to better recycling strategies and quality control in nickel processing and battery-grade materials. The study found that β Ni(OH)₂ precipitated optimally at pH 6.5, with a recovery rate of approximately 90.27% and minimal copper (79% loading efficiency) and iron impurities. Lime precipitation effectively removed Fe³⁺ at pH 2.5 and Cu between pH 4 and 6, with high removal efficiencies. Analytical methods such as EDXRF and FAAS, when calibrated, provided accurate results for trace elements, though discrepancies were noted for certain elements. The advancements in extraction and purification techniques, coupled with improved analytical methods and the novel application of NiO in VOC sensing, contribute significantly to the field of nickel recovery and processing. This research supports sustainable recycling practices and enhances the practical utility of recovered nickel, advancing both industrial applications and waste management strategies. Overall, this thesis contributes to advancing the understanding of impurity removal processes in nickel recovery and underscores the importance of precise control and characterization techniques in industrial applications.Item Application of oxidative enzymes in membrane systems for the bioremediation of triazines in wastewater(University of the Witwatersrand, Johannesburg, 2024-10) Lesaoana, Mahadi; Richards, Heidi L.; Brady, DeanThe prevalence of herbicidal pollutants present in various environmental matrices have become a global concern. The discharge and accumulation of s-triazine agrochemicals in effluents remains a major challenge, threatening the quality of freshwater resources. These are newly identified recalcitrant contaminants of concern (CECs) with complex structures, and inadvertent exposure poses deleterious ecological risks and human health-related adverse effects. Unfortunately, they have shown resistance to conventional treatment strategies, hence their persistence in wastewater treatment plant (WWTP) effluents and water bodies. Therefore, there is an urgent need for the exploration of alternative technologies for the effective eradication of such contaminants from water samples. The bioconversion of such micropollutants using oxidative enzymes like laccase is a promising research avenue, providing a sustainable, economically and ecologically benign strategy. The current research examined the potential of a hybrid biocatalytic membrane system to degrade common s-triazine agrochemical herbicides in aqueous solutions. Specifically, the use of Novoprime base 268 laccase coupled with hollow fibre polyethersulfone (PES) membranes was investigated for the bioremediation of atrazine (ATZ), ametryn (AMT), simazine (SMZ) , prometon (PMT) and terbuthylazine (TERB) in wastewater. In batch-mode reactions, major operating parameters (i.e. pH and temperature profiles, enzyme dosage and contact time) were varied for the laccase-assisted catalysis of s-triazine compounds. Optimised conditions provided highest removal efficiencies (> 88.9%) at pH 5.0, combined with a temperature of 25°C and 1.0 mg L-1 solution concentration after 24h reaction time. Through the addition of redox mediators viz. 2,2-azino-bis-3-ethylbenzothiazoline-6-sulphonic acid (ABTS), violuric acid (VA), vanillin (VA), syringaldehyde (SRA) and acetosyringone (ASR) recalcitrant triazine degradation was enhanced by 10 to 20 % at 1.50 mm. Subsequently, the performance of a standalone continuous flow-mode membrane system was evaluated firstly, using a bed adsorption column only operated under various conditions. The efficiencies were compared to batch-mode enzymatic experiments. The adsorption of triazines by PES was only weakly influenced by pH, and the optimum removal was attained at pH 5.0 (5.0 mg L-1), 2.35 g bed mass (14.0 cm height) and 24h column operation time. The overall removal percentages were 72.6%, 75.2%, 71.4%, 67.4%, and 68.2% for ATZ, AMT, SMZ, PMT and TERB, respectively. Although the results indicated satisfactory performances by both systems, their performance is limited when used as separate units (continuous membrane vs laccase reactor). A biocatalytic membrane system was achieved by integrating laccase into the dynamic packed-bed membrane column. Relevant process control design parameters of the fixed-bed biocatalytic column were carefully evaluated and recorded an optimum of 93.2 % removal efficiency as observed at a feed flow rate 2.0 mL min-1, at a bed height of 14.0 cm using an atrazine influent concentration of 5.0 mg L-1. Equilibrium dynamics of the breakthrough modelling were best fitted by Thomas model. Results attained demonstrated selectivity for triazines in matrix-matched real river water samples with remarkable recyclability after six successive operational cycles. This reflects the potential workability of the integrated system for extended enzymatic reactions evaluated under robust experimental conditions. As a benchmarking exercise, cost-analysis studies showed comparable projected scalability of our configuration at 1200 m3/d capacity at an estimated total cost of R7.036 mil.Item Energy storage properties of carbon onion-carbon nanofibre composites containing transition metal compounds(University of the Witwatersrand, Johannesburg, 2022) Khawula, Tobile Nokuphiwa Yollanda; Ozoemena, K. I.The quest for electrical energy storage has been a key driver for researchers to come up with more effective means of storing this form of energy due to the intermittent nature of renewable energy sources. Several countries have swiftly adopted the transformative potential of renewables, in particular solar energy, while others have delayed the implementation due to complex policies surrounding renewable energy projects. A way forward would be innovative regulatory approaches that encourage the pairing of solar systems with other generation technologies, and with storage, to offer a “round the clock” supply. Rechargeable batteries and supercapacitors are widely employed energy storage systems. A rechargeable battery system offers high energy density, with lithium-ion batteries (LIBs) being the most widely used. For some applications, it is imperative that energy is delivered at a much faster rate. This characteristic feature is known as power density, and supercapacitors have proven to be much better than batteries in this case. The large-scale commercialization and adoption of a supercapacitor are hindered by its low energy density. The electrode material is a major determinant of the success of supercapacitors. Generally, these are supported on high surface area carbon materials. This study focused on the development of electrospun polyacrylonitrile (PAN) fibres embedded with onion- like carbon (OLC) and iron (II) phthalocyanine (FePc) particles, and encapsulation of the fibres with Molybdenum disulphide (MoS2). Furthermore, composite fibres were either integrated with manganese (III) oxide (Mn2O3) or engineered with defects for enhanced performance in symmetric supercapacitors. The synthesis of electrode materials was divided into four phases; In the first phase (1), OLC nanoparticles were embedded in electrospun PAN fibres and decorated with the Mn2O3 and evaluated as supercapacitor electrode materials. For enhanced interfacial electrochemistry and overall capacitance, the electrode material in (1) was encapsulated with MoS2 in phase (2). In phase (3) FePc embedded in the PAN electrospun fibres were evaluated for supercapacitor applications. Limited specific capacitance and poor cycling stability were observed, thus suggesting integrating OLC and further encapsulation with MoS2, in phase (4). The morphology of the fibres was vii engineered with defects in the form of Fe2+ vacancies to maximize the electrochemical reactions of the OLC/MoS2 fibre composite. The electrochemical properties of the fibre composite materials were investigated and OLC/Mn2O3-CNF exhibited a specific capacitance, energy and power density of electrodes were 200 F g-1, 44.63 Wh kg-1 and 3 235 W kg-1, respectively with excellent capacitance retention. While the MoS2 encapsulated and Mn2O3 decorated fibre composite, OLC/MoS2@Mn2O3 displayed a specific capacitance, energy and power density of 348 Fg-1 18.42 Wh kg-1 and 5 095 W kg-1, respectively. It is pertinent to note that the capacitance of the electrodes was retained throughout the 5 000 cycles of the charge-discharge test. Upon thermal treatment at 600 °C, FePc-PAN transformed into FeN4-CMF and exhibited a specific capacitance, energy and power density of 147 F g-1, 12.48 Wh kg-1 and 4 320 W kg-1, respectively. The vacancy-rich (FeN4)d-OLC- CNF@MoS2 composite obtained by the removal of Fe2+ atoms, showed a specific capacitance, energy density and power density of 481 F g-1, 76 Wh kg-1 5833 W kg-1, respectively. This study underscores strategic processes that can be adapted in the design, synthesis and optimization of supercapacitors-based electrodes for enhanced performance.