School of Chemistry (ETDs)

Permanent URI for this communityhttps://hdl.handle.net/10539/38001

Browse

Now showing 1 - 2 of 2

A systematic study on the use of the sol-gel synthetic method for lithium manganese oxide-based cathode materials
(University of the Witwatersrand, Johannesburg, 2024-09) Muntswu, Zwivhuya; Billing, Caren; Ferg, Ernst E.; Billing, David G.
This dissertation investigated the synthesis of two lithium manganese oxide-based cathode materials (Li1.03Mn1.97O4 and LiAl0.4Mn1.6O4) using the sol-gel method and probing the phase transitions during the synthesis. The sol-gel synthetic method involved dissolving stoichiometric amounts of lithium nitrate, manganese nitrate hydrate, and citric acid in distilled water forming an aqueous solution. The starting precursor materials were dried at 140 °C which formed a crystalline phase of -Aqua-S-citrato (2-)-manganese(II) with an orthorhombic crystal system and P222 space group. The thermal behaviour of the precursor was explored to understand the effects of calcination/annealing temperatures. Thermal analysis of precursors prepared using nitrate salts with a 1:1 total metal ion to citric acid ratio displayed thermal stability to temperatures higher than 380 °C with the formation of a final metal oxide after 70% mass loss due to the decomposition of the organic and nitrate materials. However, when increasing the concentration of the complexing agent, an increase in material decomposition due to an increase in organic material is seen. The precursor materials prepared with a lower complexing agent concentration result in materials that have thermal instability when exposed to high temperatures. Thermal analysis of Li1.03Mn1.97O4 and LiAl0.4Mn1.6O4 prepared using acetate salts as starting materials shows material decomposition at high temperature of ~600 °C Calcining both undoped and Al-doped nitrate precursors at moderate temperatures (380 °C to 500 °C) resulted in the formation of Li1.03Mn1.97O4 and LiAl0.4Mn1.6O4 with a pure cubic spinel structure and an Fd-3m space group, however, increasing the calcining temperature to 800 °C for the undoped nitrate-based precursor revealed an impurity phase formation relating to dilithium manganese oxide with a monoclinic crystal system. On the other hand, calcining acetate-based precursors at moderate temperatures (380 °C to 500°C) results in metal oxides with low crystallinity compared to metal oxides prepared with nitrate-based precursors. Calcining acetate-based precursors at 800 °C was more favourable since they form the desired metal oxides without any impurities which might imply structural phase stability at high temperatures. The local and average crystallographic structures (via PDF and XRD respectively) of various nitrate-based metal oxides were investigated, where a good agreement between collected data and a calculated structural model revealed the formation of a cubic spinel structure of space group Fd-3m. Li1.03Mn1.97O4 and LiAl0.4Mn1.6O4 metal oxides were achieved from calcining precursors at moderate temperatures of 380 °C and 450 °C. The PDF high r-value signal displays a good fit which confirms to the average structure data information where the r-value signal which correspond to the local structure refinements have a minor discrepancy when fitted with a cubic spinel of space group Fd-3m.
Structural Characterization of Bimetal-Phosphate Based Solid-State Electrolytes: A PXRD, PDF and XAS Study
(University of the Witwatersrand, Johannesburg, 2024) Nkala, Gugulethu Charmaine; Billing, David G.; Billing, Caren; Vila, Fernando D.; Forbes, Roy P.
In this work, NASICON-type lithium titanium phosphate (LiTi2(PO4)3, LTP) was synthesized following the conventional solid-state reaction methodology. Single and double-doped formulations of LTP were made, with the primary objective of improving the room-temperature ionic conductivity, for their application as potential solid-state electrolytes for all-solid-state Li ion batteries. The primary characterization technique applied was ambient-temperature powder X-ray diffraction (PXRD) at both laboratory and synchrotron experimental conditions. The Rietveld refinement approach was used to determine the qualitative and quantitative phase compositions of each sample, revealing the rhombohedral (R-3c, space group #167) main phase, with phosphate-based secondary phases. Total scattering data, through the pair distribution function (PDF) was applied, revealing lattice site preference during the substitution of Ti with Al, Sn and Dy at the 12c site. Further analysis through small-box modelling indicated the local structure deviation below 10 Å, from rhombohedral (R-3c) to monoclinic (P21/n, space group #14). The application of experimental X-ray absorption spectroscopy (XAS) revealed a stable 4+ oxidation state for Ti regardless of doping. However, the extended X-ray absorption fine structure (EXAFS) data showed that the replacement of Ti with Sn results in heavy disorder and subsequent changes in the PO4 tetrahedra, corroborating the findings from Raman spectroscopy. Theoretical XAS spectra were computed using FEFF, providing insights into the origins of experimentally observed XAS features from first-principles. Applying electrochemical impedance spectroscopy (EIS) to assess the ambient-temperature ionic conductivity, co-doped systems showed an improvement in the conductivity. The application of characterization techniques at various length scales has been demonstrated to provide insights into the mechanisms governing the performance of the solid-state electrolytes.