Electronic Theses and Dissertations (PhDs)

Permanent URI for this collection

https://hdl.handle.net/10539/38002

Browse

Browsing Electronic Theses and Dissertations (PhDs) by SDG "SDG-15: Life on land"

Now showing 1 - 1 of 1
  • No Thumbnail Available
    Item
    Interfacial engineering of NbSe2 and TaSe2 to enhance their electrocatalytic activity for hydrogen production
    (University of the Witwatersrand, Johannesburg, 2023-07) Kolokoto, Tshwarela; Moloto, Nosipho
    There has been a need to replace fossil fuels, develop sustainable energy systems, and alleviate the negative environmental effects. These effects can be alleviated by developing efficient processes such as water-splitting, which can produce hydrogen gas in an environmentally friendly manner and, in turn, use it as a clean fuel. However, this process requires an effective electrocatalyst comparable to Pt and cost-effective. Herein, we demonstrate that the electrocatalytic activity of NbSe2 and TaSe2 can be improved by metal inclusion using interfacial engineering for the hydrogen evolution reaction (HER). The readily synthesised NbSe2 was decorated with 20% wt. Ni, 20% wt. Pt, 10% wt. Pt / 10% wt. Ni using two synthetic methods, namely the ex-situ and in-situ methods. The ex-situ samples had higher HER activities than the in-situ samples. Pt/PtO2-NbSe2 (derived from Pt decorated NbSe2 using the ex-situ method) showed a significantly enhanced HER activity compared to bare NbSe2. The Pt/PtO2-NbSe2 nanomaterial had the lowest overpotential, favourable kinetics and durability in an alkaline solution of 0.1 M KOH. The trend was as follows: Pt/PtO2-NbSe2 (Pt-decorated ex situ) > PtO-NbSe2 (Pt-decorated in-situ) > PtO/NiO-NbSe2 (Pt/Ni-decorated) > Ni/NiO-NbSe2 (Ni-decorated ex-situ) > Ni0.5Se/Ni(OH)2-NbSe2 (Ni-decorated in-situ) > NbSe2. In addition, NbSe2 was further decorated with 20% wt. Co using both the ex-situ and in-situ synthetic methods, and 10% wt. Pt / 10% wt. Co using the in-situ method. The ex-situ sample resulted in a higher HER activity compared to the in-situ samples. In particular, Co/Co3O4-NbSe2 nanomaterial (Co-decorated ex-situ) had the lowest overpotential, favourable kinetics and durability in an alkaline solution of 0.1 M KOH. The resultant trend was as follows: Co/Co3O4-NbSe2 (Co-decorated ex-situ) < Co3O4/CoSe2/PtO/PtO2-NbSe2 (Pt/Co-decorated in-situ) < Co3O4/CoSe2-NbSe2 (Co-decorated in-situ) < NbSe2. Consequently, the ex-situ method was the optimum synthetic method for forming NbSe2-based nanomaterials. TaSe2-based nanomaterials were formed similarly. TaSe2-based hybrids were formed by decorating TaSe2 with 20% wt. Ni, Co and Pt using the ex-situ method. The hybrid nanomaterials resulted in higher HER activities compared to pristine TaSe2 (i.e. Pt/PtO/PtO2-TaSe2 (Pt-decorated) > Ni/Ni(OH)2-TaSe2 (Ni-decorated) > Co/Co3O4-TaSe2 (Co-decorated) > TaSe2). Pt/PtO/PtO2-TaSe2 hybrid, in particular, resulted in the lowest overpotential under alkaline solutions (0.1 M KOH). Generally observed, was NbSe2-based electrocatalysts were better than TaSe2-based catalysts. In addition, the Pt-decorated ex-situ NbSe2 and Pt-decorated TaSe2 electrocatalysts were better than the model Pt/C catalyst, with the prior being the best overall. This is attributed to the basal sites of the NbSe2 and TaSe2. The ex-situ method was better than the in-situ method and this was due to the presence of metallic particles and the minimization of oxidation compared to the latter.