The effect of friction hydro-pillar processing on the properties and characteristics of ASTM grade P92 steel

Simple item page
dc.contributor.authorMoropene, Tumelo
dc.date.accessioned2022-05-31T06:51:03Z
dc.date.available2022-05-31T06:51:03Z
dc.date.issued2021
dc.descriptionA research report submitted to Faculty of Engineering and the Built Environment, University of the Witwatersrand, Johannesburg, in fulfilment of the requirements for the degree of Master of Science in Engineeringen_ZA
dc.description.abstractThe effect of the Friction Hydro-Pillar Process (FHPP) on the microstructure and hardness of P92 ferritic/martensitic steel was studied to determine whether FHPP could be used to repair cracks in the main steam pipes of power plants. The microstructural evolution, phase formation and hardness of the P92 steel were analysed. Thermo-Calc software with the TCFe5 database was used to calculate phase proportion diagrams for the P92 pipe and weld samples. Gleeble uniaxial compression tests were used to simulate the FHPP weld. Hot compression tests were done at 1100°C and 1200°C at strain rates of 10 s-1 and50 s-1 in order to simulate FHPP weld. The compressed samples were subsequently heat treated at 760°C for 3 hours 45 minutes or 5 hours because the provided FHPP welds had been heat treated. Thermo-Calc phase proportion diagrams indicated BCC as the major phase with minor amounts of M23C6, MnS, M2B, MX, FCC and Laves phases. The Gleeble uniaxial compression results showed that the flow stress increased with decreased deformation temperature and increased strain rate. The FHPP weld had good integrity without defects. The FHPP weld sample was fully tempered martensite with 254±19 HV0.3 hardness, whereas the hot compressed specimens had 449±11 HV0.3 hardness. The heat treatment reduced the hardness of the hot compressed samples to 280±29 HV0.3. Gleeble compression tests with subsequent heat treatment reproduced the FHPP weld structure. Thus, FHPP can be used to repair steam pipes because of the good integrity of the welden_ZA
dc.description.librarianCK2022en_ZA
dc.facultyFaculty of Engineering and the Built Environmenten_ZA
dc.identifier.urihttps://hdl.handle.net/10539/32951
dc.language.isoenen_ZA
dc.schoolSchool of Chemical and Metallurgical Engineeringen_ZA
dc.titleThe effect of friction hydro-pillar processing on the properties and characteristics of ASTM grade P92 steelen_ZA
dc.typeThesisen_ZA
Files
Original bundle
Now showing 1 - 2 of 2
No Thumbnail Available
Name:
ABSTRACT (1).pdf
Size:
176.27 KB
Format:
Adobe Portable Document Format
Description:
Download
No Thumbnail Available
Name:
T Moropene Msc 2021.pdf
Size:
11.56 MB
Format:
Adobe Portable Document Format
Description:
Download
License bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
license.txt
Size:
1.71 KB
Format:
Item-specific license agreed upon to submission
Description:
Download
Collections
ETD Collection