Effect of VC, Cr3C2 and Ru additives on mechanical properties of WC-10wt%Co sintered with spark plasma sintering

Simple item page
dc.contributor.authorLuthuli, Sibusiso
dc.date.accessioned2023-02-02T09:05:43Z
dc.date.available2023-02-02T09:05:43Z
dc.date.issued2022
dc.descriptionA dissertation submitted to the School of Chemical and Metallurgical Engineering, Faculty of Engineering and the Built Environment, University of the Witwatersrand, in partial fulfilment of the requirements for the degree of Master of Science (MSc), 2022
dc.description.abstractThis dissertation presents the effect of VC, Cr3C2 and Ru additives on the mechanical properties of WC-10wt% Co manufactured using spark plasma sintering (SPS). Spark plasma sintering has the advantage of being a high-speed sintering process and achieves full densification (>99%) at a lower sintering temperature than other conventional sintering techniques, thereby preventing Ostwald ripening. The study involved the characterisation of the microstructures of both powder and sintered samples morphology and phases present using optical microscopy, particle size analyser, SEM and XRD. Eight samples were made with a composition of 0.2wt% of the grain growth inhibitors (VC, Cr3C2 and Ru) and base sample of WC-10wt% Co. The powders were milled using a planetary ball mill with 4:1 ball- to-powder ratio. Powders were sintered in SPS at 1150°C for 8 minutes at 50MPa under vacuum and the relative density of all samples was above 99%. The addition of grain growth inhibitors successfully decreased the WC grain size from a maximum of 0.524 ± 0.003 μm to a minimum of 0.489 ± 0.002 μm. The binder mean free path and WC contiguity was dependent on the amount of WC/WC contact, and smaller WC grain size resulted increased Co binder between WC, thus lowering the number of WC/WC contacts. Therefore, decreasing the binder mean free path increased the hardness of the samples. Since there was an inverse relationship between binder mean free path and WC contiguity, a lower WC contiguity resulted in a lower hardness and an increase in fracture toughness
dc.description.librarianCK2023
dc.facultyFaculty of Engineering and the Built Environment
dc.identifier.urihttps://hdl.handle.net/10539/34384
dc.language.isoen
dc.schoolSchool of Chemical and Metallurgical Engineering
dc.titleEffect of VC, Cr3C2 and Ru additives on mechanical properties of WC-10wt%Co sintered with spark plasma sintering
dc.typeDissertation
Files
Original bundle
Now showing 1 - 2 of 2
Thumbnail Image
Name:
S Luthuli MSc 19 May 2022 final.pdf
Size:
3.18 MB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Cover+Abstract_900957 pdf.pdf
Size:
177.14 KB
Format:
Adobe Portable Document Format
Download
License bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
license.txt
Size:
2.43 KB
Format:
Item-specific license agreed upon to submission
Description:
Download
Collections
ETD Collection