ETD Collection

Permanent URI for this collectionhttps://wiredspace.wits.ac.za/handle/10539/104


Please note: Digitised content is made available at the best possible quality range, taking into consideration file size and the condition of the original item. These restrictions may sometimes affect the quality of the final published item. For queries regarding content of ETD collection please contact IR specialists by email : IR specialists or Tel : 011 717 4652 / 1954

Follow the link below for important information about Electronic Theses and Dissertations (ETD)

Library Guide about ETD

Browse

Filters

20061

Settings

Author: search.filters.author.Mwamba, Ilunga AlainSubject: search.filters.subject.aluminothermic

Search Results

Now showing 1 - 1 of 1
  • No Thumbnail Available
    Item
    Characterisation of Al-Ti-B grain refiners prepared by aluminothermic reduction of TiO2 and B2O3
    (2006-11-14T11:26:37Z) Mwamba, Ilunga Alain
    Microstructural characterisation was performed on Al-Ti-B grain refiners of different compositions prepared by aluminothermic reduction of TiO2 and B2O3 and dilution of the products in aluminium melts. The microstructure of the grain refiners showed needle-like TiAl3 particles as well as prismatic TiB2 particles. The TiB2 particles were coarser than those in conventional Al-Ti- B grain refiners. The microstructure also showed silicon particles and, in some cases, titanium carbide particles (TiC). The experimental grain refiners were subjected to rolling and reduced in thickness by 20, 40, 60 and 80%. The rolled samples were then heated at 625°C for 4 hours and allowed to cool slowly in the furnace. Significant changes in microstructure were noticed at 80% reduction. The flake-like and needle-like aluminide particles in the as cast microstructure were fragmented and aligned in the aluminium matrix, giving rise to short needle-like particles in parallel rows. These aluminide particles had rough edges which were rounded by heat treatment. The TiB2 particles were not affected in size or morphology by either the rolling or the heat treatment. The grain refining performance of the as cast materials was assessed. It was found that the experimental grain refiners had poorer performance than commercial grain refiners. The influence of mechanical and thermal treatments on the grain refining performance of the experimental Al-Ti-B grain refiners was also assessed. Cold working of the grain refiners had a positive influence on the grain refining performance promoting finer grain. Heat treatment of grain refiners after cold working was deleterious and led to a loss of grain refining capacity. The size and size distribution of TiB2 particles were determined related to grain refining performance and compared to theoretical models. A relationship was established between the size distribution of the TiB2 particles in the grain refiners and the grain size of inoculated aluminium. Grain refinement increased with decreasing proportion of coarse TiB2 particles in the grain refiners. This corresponded to a decrease in Ti and B contents and an increase in the Ti/B ratio.