Addition of vanadium and niobium to platinum-based alloys
Date
2013-07-23
Authors
Odera, Bernard Okich
Journal Title
Journal ISSN
Volume Title
Publisher
Abstract
The ternary systems, Pt-Al-V at the Pt-rich corner and Pt-Cr-V were investigated. Phase
equilibria data were obtained using scanning electron microscopy with energy dispersive X-ray
spectroscopy and X-ray diffraction analyses. The alloys were studied in the as-cast condition, as
well as after annealing at 1000°C for 1500 h. Solidification projections were constructed and
liquidus surface projections derived for the two systems. Isothermal sections at 1000°C were also
determined for the two systems. Two ternary phases were found in the Pt-Al-V system and one
in the Pt-Cr-V system. It was concluded that all the phase regions were identified correctly since
the results were self-consistent. Four invariant reactions were identified in the Pt-Cr-V system.
Four Pt-Al-Cr-Ru-V and two Pt-Al-Cr-Ru-V-Nb alloys were also investigated and data obtained
using scanning electron microscopy with energy dispersive X-ray spectroscopy and X-ray
diffraction analyses. The alloys were studied in the as-cast condition, as well as after annealing
at 1000°C for 1500 h. The compositions of the alloys were based on a quaternary alloy,
Pt82:Al12:Cr4:Ru2, which had been identified as one of the alloys having optimum properties in an
earlier investigation. Four of the as-cast alloys had a two-phase structure of ~Pt3Al and (Pt),
while two had a single phase, ~Pt3Al. Vanadium partitioned more to ~Pt3Al compared to (Pt).
There was an improvement in hardness compared to the quaternary alloys which had been
identified as having optimum properties.
About 64% of as-cast Pt-Al-V alloys had Vickers hardnesses higher than 500 HV0.3 while ~70%
of the annealed alloys had hardness higher than 500 HV0.3. More than 60% of both as-cast and
annealed Pt-Cr-V alloys had hardness values higher than 600 HV0.3. There was a general
increase in hardness after annealing Pt-Cr-V alloys. Hardness increased with V content in the
higher order alloys, and also the annealed alloys had higher hardness compared to the as-cast
ones.